ABSTRACT
ABSTRACT: The objective of this study was to determinate the fracture resistance of endodontically treated teeth and restored with two root post systems: i) resin post, ii) fiber post. A total of 60 teeth were freshly extracted, endodontic ally treated and randomly divided in two groups (n= 30/each group) for standardized restoration; Group 1 (Group R): Resin post and resin restoration, Group 2 (Group FP): Fiberglass post and resin restoration. Both groups' samples were mounted in a metallic base at 135º to allow them to be stabilized and held in the universal testing machine by applying a vertical force at cross speed of 1mm/min. Data were recorded in Newtons (N) Previous to test the fracture resistance; all samples were stored in distilled water at 37 ºC for 24 hours. Data were subject to the Saphiro-Wilk test for normality distribution and Student's t test. Significance was considered at 0.05 values. The values of fiber post group showed normal distribution compared to the resin group, demonstrating less variability among the values. The group FP displayed higher fracture resistance (299.77±100 N) than group R (205.57±86.40 N), with significant differences (p= 0.00002). The greatest fracture resistance was recorded for the group having fiber post reinforced and composite cores. It is suggested that fiberglass post restoration is the first option when endodontic treatment requires core restoration.
RESUMEN: El objetivo del estudio fue determinar la resistencia a la fractura de dientes tratados endodónticamente y restaurados con dos sistemas de endopostes radiculares: I) poste de resina, II) poste de fibra. Un total de 60 dientes recién extraídos fueron tratados endodónticamente y divididos al azar en dos grupos (n= 30/ cada grupo) para la restauración estandarizada; Grupo 1 (Grupo R): Pilares de resina y restauración, Grupo 2 (Grupo FP): Pilares de fibra de vidrio y restauración de resina. Las muestras de ambos grupos se montaron en una base metálica a 135º para permitir su estabilización y sujeción en la máquina universal de ensayos aplicando una fuerza vertical a velocidad transversal de 1 mm/min. Los datos se registraron en Newtons (N), para probar la resistencia a la fractura; todas las muestras se almacenaron en agua destilada a 37 ºC durante 24 horas. Los datos se sometieron a la prueba de normalidad de Saphiro-Wilk y la pruebas t de Student. La significancia se consideró con un valor de 0,05. Los valores del grupo de postes de fibra mostraron una distribución normal en comparación con el grupo de resinas, demostrando menor variabilidad entre los valores. El grupo FP mostró mayor resistencia a la fractura (299,77±100 N) que el grupo R (205,57±86,40 N) que el grupo con diferencias significativas (p= 0,00002). La mayor resistencia a la fractura se registró para el grupo que tenía núcleos compuestos y reforzados con postes de fibra. Se sugiere que la restauración posterior de fibra de vidrio es la primera opción cuando el tratamiento de endodoncia requiere una restauración del núcleo.
ABSTRACT
ABSTRACT The aim of this study was to explore the remineralizing effect of toothpastes based on Xilitol, Camellia Sinensis and Juniperus Communis. An in vitro experimental study was carried out in an 18 human premolars sample, which were treated with one of the 3 evaluated toothpastes and a control fluoride one. The atomic percentages of Ca and P were evaluated by Energy Dispersive X-ray Spectroscopy (EDS). In addition, the enamel surface of treated teeth was visualized by Scanning Electron Microscopy (SEM). The evaluations were carried out in three stages: pre-treatment, after an artificial demineralization process and after the treatment with the toothpastes. In the statistical analysis, the one-way ANOVA and Pearson correlation tests were used. Xilitol and Juniperus Communis showed the greatest gain of P ions compared to the control group (p<0.01). As for Ca, the group treated with xylitol-based toothpaste showed more ion gain compared with the control group (p<0.01). In the Pearson correlation test between Ca and P, statistically significant correlations were observed in all groups (p<0.01), ranging between r=0.7413 (Xylitol Group) and r=0.9510 (Control Group). We concluded that Xylitol paste showed the highest remineralizing property, both in the EDS analysis and in the SEM images.
RESUMEN El objetivo de este studio fue explorer el efecto remineralizante de las cremas dentales compuestas de Xilitol, Camelia Sinensis y Juniperus Communis. Se llevó a cabo un estudio experimental in vitro en una muestra de 18 premolares humanos, los cuales fueron tratados con una de las tres pastas dentales evaluadas y una fluorada. Los porcentajes atomicos de Ca y P fueron evaluados por Espectroscopia de rayos X de energía dispersive (EDS). Además, la superficie del esmalte de los dientes tratados fue examinada por Microscopia Electronica de Barrido (SEM). Las evaluaciones fueron llevadas a cabo en tres etapas: pre-tratamiento, despues de un proceso artificial de desmineralizacion y después del tratamiento con las pastas dentales. Se usaron ANOVA de una via y correlacion de Pearson para el analisis estadistico. Xilitol y Juniperus Communis mostraron la mayor ganancia de iones P comparados con el grupo control (p<0.01), con rangos entre r=0.7413 (Grupo con Xylitol) and r=0.9510 (Group Control). Se concluyó que la pasta con Xilitol mostró las mayores propiedades remineralizantes, tanto en el analisis EDS y las imágenes SEM.
Subject(s)
Tooth Remineralization/methods , Toothpastes , Xylitol/therapeutic use , In Vitro Techniques , Juniperus , CamelliaABSTRACT
Objetivo: investigar los efectos de la irradiación ultravioleta (UV) sobre placas de titanio (Ti) para la adhesión osteoblástica por medio de un método colorimétrico simple y reproducile para determinar la densidad celular. Materiales y métodos: dos diferentes tamaños (10x10x0.5 mm y 20x20x0.5 mm) de placas (n=10 c/gp) fueron obtenidas de una hoja de Ti puro y divididas en dos grupos (n=5/gp) para cada tamaño de placa. La superficie de las placas de Ti fue pulida, observada con microscopía electrónica de barrido (MEB) y estimada la rugosidad de la superficie pulida. Para el grupo experimental, las placas de Ti fueron irradiadas a una longitud de onda de 253.7 nm con luz UV durante 5, 20, 40, 60 minutos ó 4 y 6 horas. Células odontoblásticas de ratón MC3T3-E1 fueron cultivadas en medio alfa mínimo esencial (-MEM) e inoculadas sobre cada placa de Ti. El número de células adheridas y proliferadas fue determinado por medio del método MTT y el consumo de animoácidos. Resultados: 20 minutos de irradiación UV de las placas de Ti fueron suficientes para incrementar significativamente (p<0.05) la adhesión y proliferación celular, acompañado de un mayor consumo de aminoácidos. Conclusiones: la irradiación UV sobre placas de Ti incrementó significatiamente la adhesión celular por medio del método MTT, confirmando la potencialidad de la luz UV.